HARRIS 0% Welding Brazing Rod Flat Filler Metal Rod 0.05" x 1/8" x 18" (kg)
Harris O is Silver PhosCopper Brazing Alloy, economical alloy designed for brazing copper to copper connections. This alloy flows quickly at brazing temperature so requires close joint tolerance, less than 0.005" is a frequent choice for copper brazing.
Harris 0 is also a suitable choice for brazing brass. In this application operators should take care to avoid over heating the brass and use Harris Stay Silv® white brazing flux.
Harris 0 is not recommended for brazing steel or other ferrous base metals. The phosphorus content will form a low ductility intermetallic with the base metal
SPECIFICATIONS
| Dimension in Inch | 0.050" x 1/8" x 20" |
|---|---|
| Dimension in mm | 1.27 mm x 3.18 mm x 457mm |
| Flat Thickness | 1.27mm |
| Weight | Approximately 20g per stick |
| Solidus | 1310°F (710°C) |
| Liquidus | 1460°F (793°C) |
| Brazing Range | 1345°F ~ 1500°F (730°C ~ 816°C) |
| Electrical Conductivity | 9.9 (%IACS) |
| Electrical Resistivity | 19.2 |
| Compliance | AWS A5.8 BCuP-2, ASME Section IIC SFA 5.8 BCuP-2, ISO 17672 CuP 181 |
| Made in | USA |
TYPICAL APPLICATIONS
- For copper or brass
- Good for application where moderate fit-up can maintained and brazing temperature is not critical
- Recommended joint clearance .002 - .007" (0.051 - 0.177 mm)
CHEMICAL COMPOSITION
- Copper: Remainder
- Phosphorus: 7.1
- Other (Total): 0.15
WHAT'S IN THE BOX
1x HARRIS® 0% Brazing Rod Flat Filler Metal 0.05" x 1/8" x 18" (kg)
| Brand | HARRIS |
|---|---|
| Electrode Type | Brazing Alloy Filler Rod |
| Electrode / Wire Material Type | Copper |
| Classification Type | No |
| Electrode / Wire Diameter (mm) | 3.2 |
| Electrode Length (m) | 0.45 |