HARRIS Stay Silv 15 PhosCopper Brazing Alloy brazing filler metal is a frequent choice for brazing copper, especially in brazing air conditioning and refrigeration connections. The alloy has a wide melting range which allows the operator to fill loose connections and "cap" or build up around the finished joint. When heated above its liquidus temperature, however, it will flow into tight connections.
Stay Silv 15 can be used to braze brass with the use of appropriate brazing flux. Stay Silv 15 is not recommended for brazing steel or other ferrous metals due to sufficient lack of joint ductility. It is generally suitable for brazing low nickel, (10% maximum), copper/nickel base metals.
|Dimension in Inch||0.050" x 1/16" x 20"|
|Dimension in mm||1.27 mm x 1.59 mm x 508 mm|
|Brazing Range||1300°F- 1500°F (704°C -816°C)|
|Electrical Conductivity||9.9 (%IACS)|
|Compliance||ANSI/AWS A5.8 Class BCuP-5, ASME SFA 5.8 Class BCuP-5, QQ-B-654A BCuP-5, ISO 17672 CuP 284|
- Phosphorus: 4.8-5.2
- Copper: Remainder
- Silver: 14.5-15.5
- Other (Total): 0.15
WHAT'S IN THE BOX
1x HARRIS STAY-SILV 15 Brazing Rod Flat Filler Metal 51 Stick Tube 0.050" x 1/16" x 20"
|Electrode Type||Brazing Alloy Filler Rod|
|Electrode / Wire Material Type||Copper|
|Electrode / Wire Diameter (mm)||1.6|
|Electrode Length (m)||0.5|